Preparation and characterization of carbon composite plates as an electrode for alkaline fuel cell

Preparation and characterization of carbon composite plates as an electrode for alkaline fuel cell

En esta investigacin̤ se cubrieron partc̕ulas de grafito (80 æm) y politetrafluoretileno (PTFE) (40 æm) con partc̕ulas finas de nq̕uel (18-50 wt%) y PTFE (0,3 æm; 8 wt%) mediante deposicin̤ qum̕ica de un material compuesto Ni-PTFE. La conductividad del grafito (C/Ni<U+0096>PTFE) y PTFE (PTFE/N...

Mô tả đầy đủ

Đã lưu trong:
Chi tiết về thư mục
Tác giả khác: Kim Jae Ho, Yang Xi, Yonezawa Susumu, Takashima Masayuki, International Association of Structural Engineering & Mechanics (IASEM)
Định dạng: Sách
Ngôn ngữ:Tiếng Anh
Những chủ đề:
Ciencias qum̕icas
Fisicoqum̕ica
Qum̕ica
Chemical sciences
Chemistry
physical and theoretical
Recubrimientos
Materiales compuestos
Compositos
Politetrafluoretileno
PTFE
Grafito
Celdas alcalinas de combustible
Coatings
Composite materials
Composites
Polytetrafluoroethylene
Graphite
Alkaline fuel cells
Truy cập trực tuyến:Preparation and characterization of carbon composite plates as an electrode for alkaline fuel cell
Các nhãn: Thêm thẻ
Không có thẻ, Là người đầu tiên thẻ bản ghi này!
Miêu tả
Tóm tắt:En esta investigacin̤ se cubrieron partc̕ulas de grafito (80 æm) y politetrafluoretileno (PTFE) (40 æm) con partc̕ulas finas de nq̕uel (18-50 wt%) y PTFE (0,3 æm; 8 wt%) mediante deposicin̤ qum̕ica de un material compuesto Ni-PTFE. La conductividad del grafito (C/Ni<U+0096>PTFE) y PTFE (PTFE/Ni<U+0096>PTFE) recubiertos aument ̤con el contenido de Ni. Para una cantidad de 35 wt% Ni, la conductividad de C/Ni<U+0096>PTFE (300 Sm-1) fue el doble con respecto a PTFE/Ni<U+0096>PTFE. Las partc̕ulas se prensaron a presiones de 10<U+0096>500 kg cm-2 y se sometieron a calentamiento a 350 ʻC.

Những quyển sách tương tự